CARATTERISTICHE
TECNICHE DELLE LEGHE D'ORO COLORATO
|
|
|
LEGA
|
TITOLO
Carati
|
COLORE
|
Temp. FUSIONE
°C
|
Temp.
RICOTTURA °C
|
H.B.
|
d g/cm3
|
|
|
Au 75 Ag 18 Cu 7
|
18
|
VERDE
|
920
|
550
|
150
|
15,46
|
|
Au 75 Ag 19 Cu 6
|
18
|
VERDE
|
890
|
550
|
130
|
15,39
|
|
Au 75 Ag 17 Cu 8
|
18
|
VERDE
|
880
|
550
|
140
|
15,29
|
|
Au 75 Ag 15 Cu 10
|
18
|
GIALLO
|
880
|
500
|
140
|
15,19
|
|
Au 75 Ag 13 Cu 12
|
18
|
GIALLO
|
870
|
550
|
140
|
15,04
|
|
Au 75 Ag 11 Cu 14
|
18
|
ROSE'
|
850
|
550
|
160
|
14,96
|
|
Au 75 Ag 7 Cu 18
|
18
|
ROSSO
|
900
|
580
|
200
|
14,95
|
|
Au 75 Ag 5 Cu 20
|
18
|
ROSSO
|
880
|
550
|
180
|
14,96
|
|
Au 75 Ag 2 Cu 23
|
18 |
ROSSO
|
910
|
500
|
180
|
14,98
|
|
|
|
Au 585 Ag 240 Cu 175
|
14
|
VERDE
|
820
|
550
|
150
|
13,34
|
|
Au 585 Ag 210 Cu 205
|
14
|
GIALLO
|
830
|
500
|
160
|
13,20
|
|
Au 585 Ag 195 Cu 220
|
14
|
GIALLO
|
880
|
500
|
140
|
12,70
|
|
Au 585 Ag 165 Cu 250
|
14
|
ROSE'
|
880
|
550
|
200
|
13,09
|
|
Au 585 Ag 160 Cu 255
|
14
|
ROSE'
|
920
|
550
|
150
|
12,93
|
|
Au 585 Ag 125 Cu 290
|
14
|
ROSSO
|
910
|
550
|
220
|
12,98
|
|
Au 585 Ag 33 Cu 382
|
14
|
ROSSO
|
980
|
550
|
200 |
13,00
|
|
|
|
Au 333 Ag 467 Cu 200
|
8
|
VERDE
|
905
|
500
|
170
|
10,93
|
|
Au 333 Ag 450 Cu 217
|
8
|
VERDE
|
880
|
500
|
160
|
10,20
|
|
Au 333 Ag 410 Cu 257
|
8
|
GIALLO
|
925
|
500
|
150
|
10,83
|
|
Au 333 Ag 333 Cu 332
|
8
|
ROSE'
|
980
|
500
|
170
|
10,98
|
|
Au 333 Ag 150 Cu 517
|
8
|
ROSSO
|
1020
|
500
|
200
|
11,13
|
|
Au 333 Ag 47 Cu 538
|
8
|
ROSSO
|
1020
|
500
|
220
|
10,85 |
|
H.B.
= Durezza Brinnel / d = Densità
|
|
|
VALORI DEL CARICO DI SNERVAMENTO E DEL MODULO DI YOUNG PER LEGHE IN ORO |
|
|
|
TIPO
DI LEGA
|
CARICO
DI SNERVAMENTO (kg/mm2)
|
MODULO
DI YOUNG (kg/mm2)
|
|
|
|
18ct-1 incrudita
|
16
|
636
|
|
18ct-1 ricotta
|
15,4
|
50,1
|
|
18ct-2 incrudita
|
20
|
415
|
|
18ct-2 ricotta
|
14,1
|
42,3
|
|
18ct-3 incrudita
|
13,8
|
431
|
|
18ct-3 ricotta
|
13,6
|
50,2
|
|
14ct-1 incrudita
|
16,2
|
450
|
|
14ct-1 ricotta
|
13,6
|
150
|
|
14ct-2 incrudita
|
21
|
221
|
|
14ct-2 ricotta
|
17,4
|
55,7
|
|
14ct-3 incrudita
|
22,7
|
1274
|
|
14ct-3 ricotta
|
12,5
|
385
|
|
9ct-1 ricotta
|
21,8
|
99,5
|
|
9ct-2 incrudita
|
17,3
|
85,5
|
|
9ct-2 ricotta
|
16,4
|
79
|
|